(a) Type, size and service pressure. A DOT 4E cylinder is a welded aluminum cylinder with a water capacity (nominal) of not over 1,000 pounds and a service pressure of at least 225 to not over 500 psig. The cylinder must be constructed of not more than two seamless drawn shells with no more than one circumferential weld. The circumferential weld may not be closer to the point of tangency of the cylindrical portion with the shoulder than 20 times the cylinder wall thickness. Cylinders or shells closed in by spinning process and cylinders with longitudinal seams are not authorized.
(b) Authorized material.
(1) The cylinder must be constructed of aluminum of uniform quality. The following chemical analyses are authorized:
Table 1 to Paragraph (b)(1) - Authorized Materials
| Designation | Chemical analysis - limits in percent 5154 |
|---|---|
| Iron plus silicon | 0.45 maximum. |
| Copper | 0.10 maximum. |
| Manganese | 0.10 maximum. |
| Magnesium | 3.10/3.90. |
| Chromium | 0.15/0.35. |
| Zinc | 0.20 maximum. |
| Titanium | 0.20 maximum. |
| Others, each | 0.05 maximum. |
| Others, total | 0.15 maximum. |
| Aluminum | remainder. |
(2) The aluminum used in the construction of the cylinder must be as specified in Table 1 to paragraph (b)(1) of this section. Analyses must regularly be made only for the elements specifically mentioned in the table. If, however, the presence of other elements is indicated in the course of routine analysis, further analysis should be made to determine conformance with the limits specified for other elements. The cylinder manufacturer must maintain a record of intentionally added alloying elements.
(c) Identification. Material must be identified by any suitable method that will identify the alloy and manufacturer's lot number.
(d) Manufacture. Cylinders must be manufactured using equipment and processes adequate to ensure that each cylinder produced conforms to the requirements of this subpart. No defect is permitted that is likely to weaken the finished cylinder appreciably. A reasonably smooth and uniform surface finish is required. All welding must be by the gas shielded arc process.
(e) Welding. The attachment to the tops and bottoms only of cylinders by welding of neckrings, flanges, footrings, handles, bosses, pads, and valve protection rings is authorized. However, such attachments and the portion of the cylinder to which it is attached must be made of weldable aluminum alloys.
(f) Wall thickness. The wall thickness of the cylinder must conform to the following:
(1) The minimum wall thickness of the cylinder must be 0.140 inch. In any case, the minimum wall thickness must be such that calculated wall stress at twice service pressure may not exceed the lesser value of either of the following:
(i) 20,000 psi.
(ii) One-half of the minimum tensile strength of the material as required in paragraph (j) of this section.
(2) Calculation must be made by the following formula:
S = [P(1.3D2 + 0.4d2)] / (D2 − d2)
Where:
S = wall stress in psi;
P = minimum test pressure prescribed for water jacket test;
D = outside diameter in inches;
d = inside diameter in inches.
(3) Minimum thickness of heads and bottoms may not be less than the minimum required thickness of the side wall.
(g) Opening in cylinder. Openings in cylinders must conform to the following:
(1) All openings must be in the heads or bases.
(2) Each opening in cylinders, except those for safety devices, must be provided with a fitting, boss, or pad, securely attached to cylinder by welding by inert gas shielded arc process or by threads. If threads are used, they must comply with the following:
(i) Threads must be clean-cut, even, without checks and cut to gauge.
(ii) Taper threads to be of length not less than as specified for American Standard taper pipe threads.
(iii) Straight threads, having at least 4 engaged threads, to have tight fit and calculated shear strength at least 10 times the test pressure of the cylinder; gaskets required, adequate to prevent leakage.
(3) Closure of a fitting, boss, or pad must be adequate to prevent leakage.
(h) Pressure testing. Each cylinder must successfully withstand a pressure test as follows:
(1) Pressure test. All cylinders with a wall stress greater than 18,000 psig must be tested by water-jacket or direct expansion method as prescribed in CGA C-1 (IBR, see § 171.7 of this subchapter). The testing equipment must be calibrated as prescribed in CGA C-1. All testing equipment and pressure indicating devices must be accurate within the parameters defined in CGA C-1.
(i) Each cylinder must be tested to a minimum of two (2) times service pressure.
(ii) The minimum test pressure must be maintained at least 30 seconds and sufficiently longer to ensure complete expansion. Any internal pressure applied after heat-treatment and prior to the official test may not exceed 90 percent of the test pressure. If, due to failure of the test apparatus or operator error, the test pressure cannot be maintained, the test may be repeated in accordance with CGA C-1, section 5.7.2.
(iii) Permanent volumetric expansion may not exceed 12 percent of the total volumetric expansion at test pressure.
(2) Lot testing.
(i) Cylinders with a wall stress of 18,000 psig or less may be lot tested. At least one (1) cylinder randomly selected out of each lot of 200 or less must be tested by the water-jacket or direct expansion method as prescribed in CGA C-1. The testing equipment must be calibrated as prescribed in CGA C-1. All testing equipment and pressure indicating devices must be accurate within the parameters defined in CGA C-1. If, due to failure of the test apparatus or operator error, the test pressure cannot be maintained, the test may be repeated in accordance with CGA C-1, section 5.7.2.
(ii) Each selected cylinder must be tested to a minimum of two (2) times service pressure.
(iii) The minimum test pressure must be maintained at least 30 seconds and sufficiently longer to ensure complete expansion. Any internal pressure applied after heat-treatment and prior to the official test may not exceed 90 percent of the test pressure.
(iv) Permanent volumetric expansion may not exceed 12 percent of the total volumetric expansion at test pressure.
(3) Pressure testing.
(i) For cylinders with a wall stress of 18,000 psig or less, the remaining cylinders of the lot must be pressure tested by the proof pressure, water-jacket, or direct expansion test method as defined in CGA C-1. The minimum test pressure must be maintained for the specific timeframe and the testing equipment must be calibrated as prescribed in CGA C-1. Further, all testing equipment and pressure indicating devices must be accurate within the parameters defined in CGA C-1.
(ii) Each cylinder must be tested to a minimum of two (2) times service pressure and show no defect. If, due to failure of the test apparatus or operator error, the test pressure cannot be maintained, the test may be repeated in accordance with CGA C-1 5.7.2 or 7.1.2, as appropriate. Determination of expansion properties is not required.
(4) Burst testing. One (1) finished cylinder selected at random out of each lot of 1000 or less must be hydrostatically tested to four (4) times service pressure without bursting. Inability to meet this requirement must result in rejection of the lot. All testing equipment and pressure indicating devices must be accurate within the parameters defined in CGA C-1.
(i) Flattening test. After hydrostatic testing, a flattening test is required on one section of a cylinder, taken at random out of each lot of 200 or less as follows:
(1) If the weld is not at midlength of the cylinder, the test section must be no less in width than 30 times the cylinder wall thickness. The weld must be in the center of the section. Weld reinforcement must be removed by machining or grinding so that the weld is flush with the exterior of the parent metal. There must be no evidence of cracking in the sample when it is flattened between flat plates to no more than 6 times the wall thickness.
(2) If the weld is at midlength of the cylinder, the test may be made as specified in paragraph (i)(1) of this section or must be made between wedge shaped knife edges (60° angle) rounded to a 1⁄2 inch radius. There must be no evidence of cracking in the sample when it is flattened to no more than 6 times the wall thickness.
(j) Mechanical test. A mechanical test must be conducted to determine yield strength, tensile strength, elongation as a percentage, and reduction of area of material as a percentage as follows:
(1) The test is required on two (2) specimens removed from one cylinder or part thereof as illustrated in appendix A to this subpart taken at random out of each lot of 200 or fewer.
(2) Specimens must conform to the following:
(i) A gauge length of 8 inches with a width not over 11⁄2 inches, a gauge length of 2 inches with a width not over 11⁄2 inches.
(ii) The specimen, exclusive of grip ends, may not be flattened. Grip ends may be flattened to within 1 inch of each end of the reduced section.
(iii) When size of cylinder does not permit securing straight specimens, the specimens may be taken in any location or direction and may be straightened or flattened cold, by pressure only, not by blows; when specimens are so taken and prepared, the inspector's report must show in connection with record of physical test detailed information in regard to such specimens.
(iv) Heating of a specimen for any purpose is not authorized.
(3) The yield strength in tension must be the stress corresponding to a permanent strain of 0.2 percent of the gauge length. The following conditions apply:
(i) The yield strength must be determined by the “offset” method as prescribed in ASTM E 8 (IBR, see § 171.7 of this subchapter).
(ii) Cross-head speed of the testing machine may not exceed 1⁄8 inch per minute during yield strength determination.
(k) Acceptable results for mechanical tests. An acceptable result of the mechanical test requires at least 7 percent and yield strength not over 80 percent of tensile strength.
(l) Weld tests. Welds of the cylinder are required to pass the following tests successfully:
(1) Reduced section tensile test. A specimen must be removed from the cylinder used for the mechanical tests specified in paragraph (j) of this section. The specimen must be taken from across the seam; edges must be parallel for a distance of approximately 2 inches on either side of the weld. The specimen must be fractured in tension. The actual breaking stress must be a minimum of 30,000 psi. The apparent breaking stress calculated on the minimum design wall thickness must be a minimum of two (2) times the stress calculated under paragraph (f)(2) of this section. If the specimen fails to meet the requirements, the lot must be rejected except that specimens may be taken from two (2) additional cylinders from the same lot as the previously tested specimens. If either of the latter specimens fails to meet requirements, the entire lot represented must be rejected.
(2) Guided bend test. A bend test specimen must be removed from the cylinder used for the mechanical test specified in paragraph (j) of this section. The specimen must be taken across the circumferential seam, must be a minimum of 11⁄2 inches wide, edges must be parallel and rounded with a file, and back-up strip, if used, must be removed by machining. The specimen must be tested as follows:
(i) Standard guided bend test. The specimen must be bent to refusal in the guided bend test jig as illustrated in CGA C-3 (IBR, see § 171.7 of this subchapter). The root of the weld (inside surface of the cylinder) must be located away from the ram of the jig. The specimen must not show a crack or other open defect exceeding 1⁄8 inch in any direction upon completion of the test. Should this specimen fail to meet the requirements, one additional specimen must be taken from two additional cylinders from the same lot and tested. If either of the latter specimens fails to meet requirements, the entire lot represented must be rejected.
(ii) Alternate guided bend test. This test may be used as an alternate to the guided bend test. The test specimen must be in conformance with The Aluminum Association's “Welding Aluminum: Theory and Practice, Fourth Edition, 2002” (IBR, see § 171.7 of this subchapter). If the specimen fails to meet the requirements, one additional specimen must be taken from two additional cylinders or welded test plates from the same lot and tested. If any of these latter two specimens fails to meet the requirements, the entire lot must be rejected.
(m) Rejected cylinders. Repair of welded seams is authorized. Acceptable cylinders must pass all prescribed tests.
(n) Markings.
(1) Markings must be as required in § 178.35 and in addition must be stamped plainly and permanently in one of the following locations on the cylinder:
(i) On the neck, neckring, valve boss, valve protection sleeve, or similar part permanently attached to the top of the cylinder.
(ii) On the footring permanently attached to the cylinder, provided the water capacity of the cylinder does not exceed 30 pounds.
(2) Embossing the cylinder head or side wall is not permitted.
(o) Inspector's report. In addition to the information required by § 178.35, the record of chemical analyses must also include applicable information on iron, titanium, zinc, and magnesium used in the construction of the cylinder.
[Amdt. 178-114, 61 FR 25942, May 23, 1996, as amended at 62 FR 51561, Oct. 1, 1997; 66 FR 45386, Aug. 28, 2001; 67 FR 51654, Aug. 8, 2002; 68 FR 75748, Dec. 31, 2003; 69 FR 54046, Sept. 7, 2004; 74 FR 16143, Apr. 9, 2009; 85 FR 85431, Dec. 27, 2020]